Wet type sealing agent

Wet type sealing agent RE-2000 is a product made of epoxy as a main component. Lt can be used to seal wet crack part or to adhere structural injector pedestal, mighty injector pedestal or port to crack part. Lt is a epoxy putty used for sealing in metal plate reinforcing work and it is used essentially in crack repair or reinforcing work.

Features

lt has excellent adhesive power to any material including wet concrete, metal plate or wood.

Uses

Sealing for wet crack part, adhesion of structural injector pedestal, sealing agent for metal plate reinforcing part.

General property

Mechanical property

How to use

lt should be used with after mixing resin with hardener with correct mixture ratio as it is two liquids phase. Pot life may be vary from. temperature and the amount of mixture. Lt the amount of mixture is large or the temperature of the place is high, pot life and hardening time becomes fast. Particularly, make a mixture in small amount for injection in summer and increase the temperature of the resin in winter. Weigh proper amount of resin and hardener correctly (resin 0.5kg , hardener0.5kg) stir these well with hera and then apply those to wet surfaces including crack part, pedestal attaching part or metal reinforcing part for sealing (refer to low pressure injection method, high pressure injection method and injection method for metal plate reinforcing)

Equipment, instrument and cleaning agent

Use iron hera or rubber hera in sealing work. Clean the equipment or tools used immediately after working with toluene, acetone, MEK or epoxy thinner.

Precautions

1. Please wear proper safety equipments including helmet, protective glasses, gloves and working cloths when handling the agent.
2. Wipe out immediately and wash with soaping water when skin is stained with the agent.
3. Please show a doctor if there is eruption of skin by staining with the agent.
4. Install a ventilator at working place to get fresh air.
5. Keep correct mix ration when mixing resin and hardener in case of two component type grouter.
6. Clean out instruments or equipment used for working with thinner etc.
7. Mix smaller amount of resin in summer as pot life, drying time, hardening time of epoxy resin may differ by temperature or mixing amount. increase the temperature of resin in winter season.
   Pot life : Time period of work with the mixture of resin and hardener.
   Drying time : Time period from the property of mixed resin begins to change to the time of hardening . After this time, we can not work with the mixture.
   Hardening time : The time to get mechanical strength as the agent hardens completely ( it should be at least 7 days and final strength can be measured at this time).
8. Do not use if it is below than 5℃ except unavoidable situation.
9. Please refer to MSDS (Material Safety Data Sheet) for proper handling.

How to keep

Keep it dry and cool place without moisture after sealing the cover to prevent contacting with the air. Proper keeping temperature is 15~30℃ Keeping period of the liquid is 6 months. However , use the agent as soon as possible as it may deteriorate by keeping condition.