DESCRIPTION

Hydrostatic press stone filmless maintenance agent is a maintenance hybrid comprised of a special kind of Oligomer Silsesquiloxane mixed in a water-based solution, 

formulated with powerful surfactants attributing to its excellent-resistance properties

and a non-yellowing methyl silane hybrid, which reacts with the moisture and 

CO2 in the air,  forming a nonsolvent based resin that penetrates into the substrate 

heightening its water proofing ability.

Its ability to penetrate deep into the concrete, as deep as 3~5m/m, distinguishes it 

from other products on the market. Moreover, it can cause a chemical reaction with

alkaline materials that produces crystals inside the concrete, that can fill and block the micro-vein within the concrete so as to reach the waterproof effect in depth; 

thus, the longevity of the building can be extended.

APPLICATION

Water, anti-pollutants and anti-weathering resistance for various surfaces such as: 

tiles, gaps between tiles, terra cotta, calcium silicate board , plasterboard ,bricks,

concrete, natural and process stone, stone carving, stone washing, stone smoothening, stone cutting,sidewalks, parking plywood.

USAGE

1. Any cracks have to be filled and all surfaces must be cleaned and dried.

    In order to permeate thoroughly for this product, one has to eliminate

    all dust, loose parts, grease, moles and old paints on the substrates,

    and the substrate itself has to be completely dry.

2. Using brush or roller to continually cure back and forth one time to finish, then the

    surface of the finished product can＇t contact with water after 

    staying-dry for 24 hours.

3. Coating area: about 5-10m 2 /1KG (vary based on absorbing rate of stones)

4. Tools suggested for use: brush, roller, spray guy

5. It is suggested that constructors should wear some protection gears like helmet, 

    rubber gloves and goggles

6. Storage: stored under shady and cool place, avoid direct sunray, valid for one year.

Additional information

■ Dilution is not allowed

■ If application of two coats is needed,

   the second coating has to be done before the first is dry.

   Before the cured substrates are completely dry, it is not allowed to place the 

   stones by piles.

■ If using on the dark stone with porous and high-hygroscopicity nature, 

   it is suggested to dilute it 1 to 2 times more.