High quality die & tool steel plate H13 / 1.2344 / SKD61 steel 
 

1.Comparable of steel plate H13 
 

H13(USA,ASTM);DHA1(Datong,Japan);4Cr5MoSiV1(China);1.2344(Germany DIN);SKD(Japan,JIS)

2.Chemical Composition(%) of steel plate H13 
 

No.

 C

Si

 Mn

 P

 S

 Cr

 Mo

 V

4Cr5MoSiV1

0.32-0.45 

0.80-1.20

0.20-0.50

≤0.030

≤0.030

4.75-5.50

1.10-1.75

0.80-1.20

H13

0.32~0.45

0.80~1.20

0.20~0.50

≤0.030

≤0.030

4.75~5.50

1.10~1.75

0.80~1.20

SKD61

0.32~0.42

0.80~1.20

≤0.50

≤0.030

≤0.030

4.50~5.50

1.00~1.50

0.80~1.20

1.2344

0.37~0.42

0.90~1.20

 0.30~0.50

≤0.030

≤0.030

4.80~5.50

1.20~1.50

0.90~1.10

3.Characteristic of steel plate H13 
 

Harden and air cooling steel, 600`C work, high rigidity, high endurance, anti-heating, anti-cracking, electric sediment and middle-melting steel, compact structure, refined in electric cooker, quality of steel is pure, owned good character of equal direction.

4.Application of steel plate H13 
 

1. Extrusion mold of aluminum and magnesium, die-casting mold, especially adapt to the mold in large and complicated form.

2. Extrusion mold of copper alloy, die-casting mold,pressing mold,plastic thin wall mold
 

3. Hot pressing machine mold

5.Heat Treatment of steel plate H13 
 

1.Quench:1000-1040`C via 600`C and 850`C, preheating oil or wind cooling

2.Temper temperature and rigidity HBC(reference):   

 quench hardening

 108-300 °c

450-500 °c

550-5700°c

53-55    

    51-52

 53-54  

 50-52

3.Temper temperature should be higher than working temperature in order to stabilize the working size of mold

4.Heat up to 650  °c of average temperature in order to eliminate the machined stress, 500  °c air cooling after electric cooker cooling      

5.Tempering, 800-850  °c ,slow cooling after diathermia

6.Melting Process of SKD61 steel rod  

1.EAF: Electric Furnace+LF+VD(Optional)

2.ESR:  Electric Furnace+LF+VD+Eleroslag Remelted(Optional)

7.UT Class of SKD61 steel rod

According to Standard of SEP 1921/84,100% Volume, Level C/c, D/d or E/e

6.Specification of steel plate H13 
 

Roundbar:

Thickness: Max:800mm, Length:3000~5800mm

Flat bar:

Thickness: Max:800mm,Width: 205~810mm,Length:2000~4000mm